DRJ Dent Res J Dental Research Journal Dental Research Journal

This is an open access journal, and articles are distributed under the terms of the Creative Commons Attribution-NonCommercial-ShareAlike 4.0 License, which allows others to remix, tweak, and build upon the work non-commercially, as long as appropriate credit is given and the new creations are licensed under the identical terms.

 1735-3327 2008-0255 Wolters Kluwer India Pvt. Ltd. India DRJ-18-14 10.4103/1735-3327.311421 Original Article Effect of cavity design and material type on fracture resistance and failure pattern of molars restored by computer-aided design/computer-aided manufacturing inlays/onlays Alassar Roqaia M Samy Amira M Abdel-Rahman Fatma M Department of Crowns and Bridges, Faculty of Dental Medicine for Girls, Al-Azhar University, Nasr City, Cairo, Egypt Department of Conservative Dentistry, Faculty of Oral and Dental Medicine, Modern University for Technology and Information, Cairo, Egypt Department of Dental Materials, Faculty of Dental Medicine for Girls, Al-Azhar University, Nasr City, Cairo, Egypt Address for correspondence:Roqaia Alassar, Department of Crowns and Bridges, Faculty of Dental Medicine for Girls, Al-Azhar University, Nasr City, Cairo, Egypt roqaiaalassar.26@azhar.edu.eg Jan–Dec 2021 18 1 14 14 3 5 2019 Copyright: © Dental Research Journal 2021

This is an open access journal, and articles are distributed under the terms of the Creative Commons Attribution-NonCommercial-ShareAlike 4.0 License, which allows others to remix, tweak, and build upon the work non-commercially, as long as appropriate credit is given and the new creations are licensed under the identical terms.

 Background:

The maximum conservation of tooth structure and the use of restorative materials with elastic modulus close to the dental structure may promote greater longevity of the tooth/restoration complex. This study was conducted to evaluate the effect of cavity design and material type on fracture resistance and failure pattern of molars restored by computer-aided design/computer-aided manufacturing (CAD/CAM) inlays/onlays.

 Materials and Methods:

In this in vitro study, 55 human maxillary molars were embedded in resin blocks and divided into control group (CG) and five main groups: Group 1: Inlay, Group 2: Conventional onlay/mesiobuccal (MB), Group 3: Conservative onlay/MB, Group 4: Conventional onlay/MB and distobuccal (DB), and Group 5: Conservative onlay/MB and DB. Then, each group was divided into two subgroups: (A) CeraSmart (CS) and (B) Katana Zirconia (KZ). Restorations were cemented by RelyX Ultimate and then thermocycled. The universal testing machine was used to measure fracture loads. Failure was determined using a magnifying lens. Data were statistically analyzed using ANOVA followed by Tukey's post hoc test (P < 0.05).

 Results:

Group 5 showed the highest significant fracture load, whereas the least significant value was recorded in Group 2. KZ recorded higher significant fracture loads than CS in all tested groups. Groups 1, 2, and 3 restored by CS showed lower fracture load than CG, but the difference was insignificant with Group 1. CS restorations showed restorable failure, while unrestorable pattern was predominant in KZ restorations (P < 0.05).

 Conclusion:

KZ inlays and onlays can be used safely in terms of fracture resistance as both have values exceed the physiologic requirements. CS inlays and onlays/MB and DB are of fracture resistance comparable to intact teeth. The use of conservative onlay design with more cusp coverage guarantees better resistance of CS restorations. Being force absorbing material, the predominant failure of teeth restored by CS was restorable.

 Ceramics computer-aided design onlays </sec> <sec> <title>Introduction

Computer-aided design/computer-aided manufacturing (CAD/CAM) esthetic restorations have more advantages than direct composite restorations; simply because of a wide range of ceramic varieties of higher fracture strength that can be selected. In addition, improved dental laboratory processing, quick fabrication, and the accuracy of restorations encourage many practitioners to shift from direct composite to CAD/CAM restorations. 1 , 2 For unsatisfactory restorations or extensive carious lesions in molars, the use of ceramics with adhesive techniques achieves the concept of conservation and offers more esthetic restorations. 3

On restoring posterior teeth, which cavity design and material type guarantee high fracture resistance along with favorable failure pattern; conventional or conservative design, and rigid or force-absorbing flexible material? The question asked by many practitioners.

It is advisable to consider the mechanical properties of the restorative materials, followed by cavity designing. 4 , 5 , 6 Particularly, modulus of elasticity has to be considered as high elastic modulus materials tend to accumulate stresses; while materials of low elastic modulus absorb stresses. 7 Therefore, Katana Zirconia (KZ) ML HTand CeraSmart (CS) as two ceramic materials of extremely different Elastic Modulus were suggested to study the difference in both material behavior under load.

Multi-layered High translucency KZ (KZ ML HT, Kuraray Noritake Dental Inc.,) discs can be used for fabricating full contour crowns, bridges, veneers, frameworks, inlays, and onlays. 8 Katana HTprovides esthetic appearance, superior strength (1100 MPa), high modulus of elasticity (210 GPa), excellent mechanical performance, and easy milling properties with higher precision compared to other ceramic. 8 , 9

CS (GC, Alsip, USA) force absorbing flexible nano ceramic CAD/CAM block combines the best characteristics of high strength ceramic and a unique esthetic of composite. It is composed of 71 wt. % silica (20 nm) and barium glass (300 nm) nanoparticles. 10 Full homogeneous and even distribution of nanoceramic network leads to unique elastic modulus similar to that of dentin (18 ± 2 GPa). 11 According to the manufacturer, uniform scuttle (very short interparticle distance) of silanated and bonded particles is the factor of acceptable marginal accuracy and high flexural strength (220 MPa). 10 , 11 , 12

Cavity design in molars covering one or more than one cusp seems to be the most controversial point. According to the number of cusps involved in the preparation, the restorations can be classified as inlays (all cusps are intact), onlays (one or more cusps are involved), or overlays (all cusps are involved). 13 In addition, the cavity width and depth may influence cusp deflection, and consequently tooth resistance to fracture. 14

The fracture resistance of molars restored with lithium-disilicate and zirconia inlays/onlays was evaluated. 13 It was concluded that cuspal coverage decreased fracture resistance of the tooth/restoration complex. Molars restored with zirconia inlays/onlays showed similar fracture resistance to intact teeth. In general, the failure patterns in lithium-disilicate samples were limited to the restoration itself. In contrast, the failure of zirconia samples involved both the tooth and the restoration. 13

In addition, the effect of cavity design and ceramic type on the fracture resistance of CAD/CAM onlays in molars was studied. The conservative onlays exhibited increased fracture resistance and more favorable failure modes. It was concluded that molars restored with lithium disilicate CAD/CAM ceramic onlays exhibited higher fracture resistance than molars restored with leucite CAD/CAM ceramic onlays. 15

The objective of this in vitro study was to compare the effect of CS and KZ ML HTon fracture resistance and the failure pattern of molars received different inlay/onlay cavity designs. The null hypothesis tested was that cavity design and material type have no influence on fracture resistance and failure pattern of molars restored by CS and KZ ML HTinlays/onlays.

 Materials and Methods

To conduct the present in vitro study, 55 freshly extracted caries-free human maxillary 1 stmolars were selected in accordance with guidelines from Research Ethics Committee approval of Faculty of Dental Medicine for Girls, Al Azhar University. The teeth were rinsed thoroughly under running water, cleaned, and stored in 0.1% thymol sol until use. The teeth were embedded in epoxy resin (East Coast Resin, USA) blocks up to 1 mm below the cementoenamel junction (CEJ).

Samples grouping

The teeth were randomly divided into intact teeth as a CG (n = 5) and five main groups (n = 10) according to cavity design: Group 1: Inlay design (I), Group 2: Conventional onlay with mesiobuccal (MB)-cusp coverage (Conv O MB), Group 3: Conservative onlay with MB-cusp coverage (Cons O MB), Group 4: Conventional onlay with MB and distobuccal (DB)-cusp coverage (Conv O MB and DB), and Group 5: Conservative onlay with MB and DB-cusp coverage (Cons O MB and DB). Then, each main group was further divided into two subgroups (n = 5) according to material type; a) CS, and b) KZ ML HT.

Cavity preparations

All samples received standardized mesio-occluso-distal (MOD) inlay preparations, in accordance with general principles for esthetic inlay restorations. 16 For conservative onlay designs, MB and DB cusps were prepared with the shoulder finish line Figure 1.

Cavity designs investigated in the study.

Figure 1

Cavity preparation guidelines

Computer Numerical Control (CNC milling machine, USA) with two diamond stones selected from the Inlay/Onlay preparation Kit (Zhengzhou Smile Dental Equipment Co., China) was used to standardize all preparations. The occlusal cavity occupied buccolingually (4 ± 1 mm) and mesiodistally (7 ± 1 mm). The depth was 2 mm measured from central groove. Proximal cavities were extended with flared buccal and lingual walls (5 mm). The proximal box was 4 mm long and 1.5 mm deep. Occlusal divergence angle was set at 10°–12°. Cavosurface margins were finished in butt joints (90°) with no bevels. Internal line and point angles were rounded. MB and DB cusps were 2 mm occlusally reduced with butt joint for conventional onlay design, and with 1 mm cusp shoulder for conservative design. Prepared dentin was sealed with an adhesive system (Single bond, 3M, USA) to prevent contamination.

Restorations construction

CAD/CAM Roland system (DWX-51D Roland DG Co., Japan) was used for the construction of all restorations in this study. Five CS and five KZ restorations were constructed from CS blocks (CS TMuniversal GC, Europe) and KZ HTmonolithic multi-layered disc (Kuraray Noritake Dental Inc., Japan), respectively, according to the following procedure Figure 2.

Restorations construction; (a) Three-dimensional digital image, (b) Designing, (c) CeraSmart blocks fixed in Roland Machine, and (d) Katana Zirconia disc in Roland Machine.

Figure 2

(1) Each sample was sprayed with light-reflecting powder (Occlutec, Scan spray. Renfert GmBh. USA), and secured on the tray of smart optics-three-dimensional-scanner (scan Box, Germany) for scanning. (2) Data were transferred to the computer connected to milling machine to start designing. The fully anatomical inlay/onlay design was formed according to the manufacturers' directions and software recommendations. (3) Milling of CS blocks and KZ disc was then activated. After milling, KZ restorations were sintered in Tabeo sintering furnace (TABEO, Germany) at 1550°C for 8 h. Then, each restoration was examined using magnifying lens (10X, Optics Co., Ltd., China) and checked for complete seating on its corresponding model. (4) CS restorations were finished and polished using coarse and fine silicone points (GC America Inc., USA) and diapolisher paste (GC America Inc., USA), with low speed handpiece, according to the manufacturer recommendations. On the other hand, a silicon diamond point (Kuraray Dental Inc., Japan) and pearl surface Z (Kuraray Noritake Dental Inc., Japan) were used for finishing and polishing of KZ restorations.

Cementation of restorations

All restorations were cemented using RelyX Ultimate resin cement (3M, ESPE, Germany) after surface conditioning of tooth structure and intaglio surfaces of constructed inlays and onlays, in accordance with their respective manufacturers' instructions.

The prepared cavities were etched for 15 s with Blue Etch (36% phosphoric acid, StalowaWola, Polska) then rinsed, dried, and bonded with double coat of Single bond (3M, ESPE, Germany).

CS intaglio surfaces were etched with 5% hydrofluoric acid gel (Ivoclar, Germany) for 60 s then washed in an ultrasonic cleaner (Senden, Germany) and dried. A ceramic primer-containing silane coupling agent (Bisco, USA) was applied and allowed to dry for 60 s.

KZ intaglio surfaces were sandblasted using alumina particles (50 μm), then cleaned in an ultrasonic cleaner and dried. A ceramic primer (Bisco, USA) was applied and allowed to react for 20 s Figure 3.

Silanization of intaglio surfaces of restorations before cementation.

Figure 3

RelyX Ultimate, the dual-cure resin cement (3M, ESPE, Germany) was applied on the prepared cavities. Then, each restoration was bonded to its corresponding cavity with finger pressure; excess cement was removed immediately with a microbrush. A load applicator of 3 Kg then used to apply constant load for full seating of restorations, then each surface was light cured for 20 s according to the manufacturer's instructions.

After cementation, samples were stored for 24 h in distilled water at 37°C, then thermocycled in automatic thermal cycling machine (Ropota, automated thermocycling, Turkey) for 5000 cycles in two water baths at 5 and 55°C.

Testing procedures

All samples were individually mounted on a computer controlled materials testing machine (Model 3345; Instron Industrial Products, Norwood, MA, USA) with a load cell of 5 kN and data were recorded using computer software (Instron ®Bluehill Lite Software). Samples were secured to the lower fixed compartment of the testing machine by tightening screws. Fracture test was done by compressive mode of load applied occlusally using a metallic rod with round tip (3.8 mm diameter) attached to the upper movable compartment of testing machine traveling at crosshead speed of 1 mm/min with tin foil sheet in-between to achieve homogeneous stress distribution and minimization of the transmission of local force peaks. 17 The load at failure manifested by an audible crack and confirmed by a sharp drop at the load-deflection curve recorded using computer software (Bluehill Lite Software Instron ®Instruments). The load required to fracture was recorded in Newton Figure 4.

Fracture resistance test in universal testing machine.

Figure 4

Failure mode assessment

The fractured samples were examined for the detection of failure pattern using a magnifying lens (10X, Optics Co., Ltd., China). The failure mode was assessed based on previous publications, 13 , 18 as follows: Type (1): restoration fracture, Type (2): Restorable tooth fracture, including cracks and/or cusp fractures, horizontal fractures, oblique fractures not reaching the CEJ, Type (3): Unrestorable fractures, including vertical fractures or oblique fractures violating the CEJ, and Type (4): Combined fracture in both tooth and restoration.

Statistical analysis

The data were analyzed using IBM SPSS software package version 20.0. (Armonk, NY: IBM Corp). The Kolmogorov–Smirnov test was used to test the normality of distribution. Quantitative data were described as a mean and standard deviation. Student's t-test was used to compare between CS and KS within the same group. F-test (ANOVA) was used for comparison between different groups of onlay and inlay (control). A P < 0.05 was considered as statistically significant.

 Results

Statistical analysis of fracture resistance test

Comparison between subgroups within the same group

In all groups, the significantly higher mean fracture resistance values were recorded in KZ restorations compared to CS restorations Table 1and Figure 5, Figure 6, Figure 7.{Table 1}

Bar chart showing mean maximum load (n) in CeraSmart group.

Figure 5

Bar chart showing mean maximum load (n) in Katana Zirconia group.

Figure 6

Bar chart showing mean maximum load (n) in CeraSmart and Katana Zirconia subgroups.

Figure 7

Comparison between different groups and control

CeraSmart

Comparing groups restored by CS revealed that the highest mean value was recorded in Group 5, whereas the least value was recorded in Group 2. CG recorded a higher value than Groups 1, 2, and 3. ANOVA test revealed that the difference between groups was statistically significant (P < 0.0001). Tukey's post hoc test revealed no significant difference between control and Groups 1 and 4. Group 1 was not significantly different from Groups 2 and 3. Moreover, there was no significant difference between Groups 2 and 3. Groups 4 and 5 were not significantly different Table 2, Table 3and Figure 5, Figure 6, Figure 7.{Table 2}{Table 3}

Katana Zirconia

Comparing groups restored by KZ revealed that the highest mean value was recorded in Group 5, whereas the lowest value was recorded in Group 2. CG recorded the least mean value among all groups. ANOVA test revealed that the difference between groups was statistically significant (P < 0.0001). Tukey's post hoc test revealed no significant difference between control and Groups 1 and 2. Group 1 was not significantly different from Group 2 Table 2and Table 3, Figure 5, Figure 6, Figure 7.

Failure pattern analysis

The most common failure pattern in CS restorations was restorable, whereas unrestorable failure pattern was the predominant in KZ restorations Table 4.{Table 4}

 Discussion

On restoring posterior teeth, the clinician always thinks how to gain maximum strength where extensive masticatory forces are applied. The use of some types of ceramics remains limited in the posterior region. 19 Gaining strength can be achieved by proper material selection and optimum cavity design, as well.

Inlay and onlay designs greatly support the treatment philosophy of minimal intervention as up to 70% of the coronal tooth structure is removed when teeth are prepared for a full-coverage crown, whereas less than half of this percentage is required to be removed for an onlay. 20

The results of this study revealed that cavity design and material type had a significant effect on fracture resistance of molars restored by CAD/CAM inlays and onlays. Therefore, the null hypothesis was rejected.

Regarding cavity design, there were no significant differences in fracture resistance values between the inlay design and intact teeth. These results are in accordance with Harsha et al., 8 Saridag et al., 13 and Cubas et al. 21 studies. This might be attributed to the little quantity of tooth structure removed during inlay preparation. 13 Furthermore, according to various in vitro studies, 13 , 21 , 22 adhesive cementation of inlay in place, regained stability of the prepared tooth and explained the high fracture resistance values of KZ inlay restoration. Moreover, it was found the elastic modulus of the resin cement may also affect the fracture strength values of the teeth restored with ceramic inlays and onlays. 21 Adhesive cements with higher elastic modulus increased the fracture strength values of inlay and onlay restorations. 21

In this study, the teeth received conservative onlay designs with MB-or MB and DB-cusp coverage showed higher fracture resistance compared to those received conventional designs with MB-or MB and DB-cusp coverage, respectively. The shoulder margin in the conservative design seemed to have the effect of ferrule resulted in better stress distribution. 23 , 24 This agreed with Oyar and Durkan 24 who concluded that cavity designs with shoulder margins showed the highest fracture resistance, whereas butt joint designs had the lowest fracture resistance. However, the difference was material related as it was significant between KZ restorations and insignificant between those restored by CS.

In both subgroups (CS and KZ), as the preparation amount was increased, (i.e., from inlay to onlay with MB-cusp design) the fracture resistance was decreased. These results coincided with Saridag et al. study, 13 in which cusp coverage decreased the fracture resistance of molars restored by lithium-disilicate onlays. However, as the preparation amount was increased to involve the DB cusp, (i.e., from onlay with MB-cusp coverage to onlay with MB and DB-cusp design) the fracture resistance was increased significantly in KZ subgroups and insignificantly with CS restorations. This may be explained by increasing restoration's surface area that related directly to mechanical properties of the restorative material used. 13

These findings were supported by Harsha et al. 8 who confirmed that increase cuspal coverage had shown a significant increase in the fracture resistance than the sound teeth. On the contrary, Cubas et al., 21 Stappert et al., 25 and Yoon et al., 26 reported that cuspal coverage had no influence on improving the fracture resistance.

Regarding the material type, teeth restored by KZ recorded significantly higher fracture resistance compared to intact teeth and those restored by CS. This was expected because zirconia, the strongest and toughest of all dental ceramics, has a flexural strength of 800–1200 MPa that meets the mechanical requirements for high stress-bearing posterior restorations. 27 , 28 Due to its strength and esthetic properties, KZ ML HTwas selected in the present study. The fracture resistance values of KZ obtained in the present study (1745.2 N-3122.4 N) indicates that KZ inlay and onlay restorations are able to withstand the high masticatory forces associated with bruxism and other parafunctions.

Although the teeth restored by CS showed the lowest fracture resistance, conservative onlay design with MB and DB-cusp coverage recorded higher fracture resistance than intact teeth. Therefore, according to the present study, it was recommended to use CS with conservative design and more cusp coverage to gain higher fracture resistance. However, the difference was insignificant.

In the current study, all samples recorded fracture load values above 1024 N that exceeded the maximum biting force of 700–900 N for posterior single teeth reported in the literature. 29 , 30 It was difficult to compare these values to previous studies due to great deviations caused by different types of ceramics used, different test methods and different preparation designs. 15

On examination of fractured samples, it was clearly observed that the most common failure mode of the teeth restored by KZ was unfavorable fracture (i.e., un-restorable), whereas restorable failure was the predominant in CS subgroups. This may be related to the high Elastic Modulus of zirconia. 31 Zirconia is considered a stiff material that transmits stresses to the underlying tooth structure that leads to unfavorable failure. In contrast, the unique composition of CS allows the material to have modulus of elasticity similar to that of dentin (18 ± 2 GPa), 31 absorbs forces and equally distributes stresses, leading to favorable failure. 12

In addition to small sample size, the limitation of the study is that no mechanical loading was applied as part of the artificial aging process, which would have provided insight into its negative effects on mechanical properties.

 Conclusion

Within the limitations of this study, the following could be concluded:

Fracture resistance and failure pattern of teeth restored by CAD/CAM inlays and onlays are greatly affected by cavity design and material type

CS inlays and onlays with MB and DB-cusp coverage are all of fracture resistance comparable to intact teeth

Regardless cavity designs, the teeth restored by KZ ML HThave the best fracture resistance

Conservative onlay design guarantees higher fracture resistance

The more cusp coverage, the higher fracture resistance of teeth restored by CS and KZ ML HTonlays, and

Being force absorbing flexible material, the predominant failure pattern of teeth restored by CS was restorable.

Acknowledgments

The authors would like to thank Prof. Dr. Mona H. Mandour, Professor of Crowns and Bridges, Faculty of Dental Medicine for Girls, Al-Azhar University, for comments that greatly improved the manuscript.

Financial support and sponsorship

Nil.

Conflicts of interest

The authors report no conflicts of interest. The authors alone are responsible for the content and writing of this article.

 Giordano R McLaren EA Ceramics overview: Classification by microstructure and processing methods Compend Contin Educ Dent 682 4, 686, 688 Yüksel E Zaimoğlu A Influence of marginal fit and cement types on microleakage of all-ceramic crown systems Braz Oral Res 261 6 Veneziani M Posterior indirect adhesive restorations: Updated indications and the morphology driven Preparation technique Int J Esthet Dent 204 30 Carvalho MA Lazari PC Gresnigt M Del Bel Cury AA Magne P Current options concerning the endodontically-treated teeth restoration with the adhesive approach Braz Oral Res e74 Ţălu S Alb SF Pârvu AE Dudea D Lainović T Gasparik C Factors influencing the choice of dental material and procedure for crown restoration of posterior teeth – Design of a “decision guide” HVM Int J Bioflu&# 141 7 Frankenberger R Hehn J Hajtó J Krämer N Naumann M Koch A Effect of proximal box elevation with resin composite on marginal quality of ceramic inlays in vitro Clin Oral Investig 177 83 O¨zkir SE Effect of restoration material on stress distribution on partial crowns: A 3D finite element analysis J Dent Sci 311 7 Harsha MS Praffulla M Babu MR Leneena G Krishna TS Divya G The effect of cavity design on fracture resistance and failure pattern in monolithic zirconia partial coverage restorations – An in vitro study J Clin Diagn Res ZC45 8 Mehl C Ludwig K Steiner M Kern M Fracture strength of prefabricated all-ceramic posterior inlay-retained fixed dental prostheses Dent Mater 67 75 Lauvahutanon S Takahashi H Oki M Arksornnukit M Kanehira M Finger WJ In vitro evaluation of the wear resistance of composite resin blocks for CAD/CAM Dent Mater J 495 502 Gulec L Ulusoy N Cengiz E Indirect resin composite restorations fabricated with chair-side CAD/CAM systems Cumhuriyet Dent J 247 55 Awada A Nathanson D Mechanical properties of resin-ceramic CAD/CAM restorative materials J Prosthet Dent 587 93 Saridag S Sevimay M Pekkan G Fracture resistance of teeth restored with all-ceramic inlays and onlays: An in vitro study Oper Dent 626 34 Al-Thobity AM Altaher A Alharbi A Elnour M An in vitro comparison of the fracture resistance of standard and modified mesio-occluso-distal cavity designs restored with resin composite restoration Int J Health Sci (Qassim) 26 30 Vianna AL Prado CJ Bicalho AA Pereira RA Neves FD Soares CJ Effect of cavity preparation design and ceramic type on the stress distribution, strain and fracture resistance of CAD/CAM onlays in molars J Appl Oral Sci e20180004 Rocca GT Rizcalla N Krejci I Dietschi D Evidence-based concepts and procedures for bonded inlays and onlays.Part II Guidelines for cavity preparation and restoration fabrication Evidence-based concepts and procedures for bonded inlays and onlays Part II Guidelines for cavity preparation and restoration fabrication Int J Esthet Dent 2015;10:392-413 Schultheis S Strub JR Gerds TA Guess PC Monolithic and bi-layer CAD/CAM lithium-disilicate versus metal-ceramic fixed dental prostheses: Comparison of fracture loads and failure modes after fatigue Clin Oral Investig 1407 13 Salameh Z Ounsi HF Aboushelib MN Al-Hamdan R Sadig W Ferrari M Effect of different onlay systems on fracture resistance and failure pattern of endodontically treated mandibular molars restored with and without glass fiber posts Am J Dent 81 6 Silva LH Lima E Miranda RB Favero SS Lohbauer U Cesar PF Dental ceramics: A review of new materials and processing methods Braz Oral Res e58 Edelhoff D Ahlers MO Occlusal onlays as a modern treatment concept for the reconstruction of severely worn occlusal surfaces Quintessence Int 521 33 Cubas GB Habekost L Camacho GB Pereira-Cenci T Fracture resistance of premolars restored with inlay and onlay ceramic restorations and luted with two different agents J Prosthodont Res 53 9 Yu W Guo K Zhang B Weng W Fracture resistance of endodontically treated premolars restored with lithium disilicate CAD/CAM crowns or onlays and luted with two luting agents Dent Mater J 349 54 Schmidlin PR Stawarczyk B DeAbreu D Bindl A Ender A Ichim IP Fracture resistance of endodontically treated teeth without ferrule using a novel H-shaped short post Quintessence Int 97 108 Oyar P Durkan R Effect of cavity design on the fracture resistance of zirconia onlay ceramics Niger J Clin Pract 687 91 Stappert CF Att W Gerds T Strub JR Fracture resistance of different partial-coverage ceramic molar restorations: An in vitro investigation J Am Dent Assoc 514 22 Yoon HI Sohn PJ Jin S Elani H Lee SJ Fracture resistance of CAD/CAM-fabricated lithium disilicate MOD inlays and onlays with various cavity preparation designs J Prosthodont e524 9 Homaei E Farhangdoost K Tsoi JK Matinlinna JP Pow EH Static and fatigue mechanical behavior of three dental CAD/CAM ceramics J Mech Behav Biomed Mater 304 13 Al-Amleh B Lyons K Swain M Clinical trials in zirconia: A systematic review J Oral Rehabil 641 52 Flanagan D Bite force and dental implant treatment: A short review Med Devices (Auckl) 141 8 Koc D Dogan A Bek B Bite force and influential factors on bite force measurements: A literature review Eur J Dent 223 32 Al-shibri S Elguindy J Fracture resistance of endodontically treated teeth restored with lithium disilicate crowns retained with fiber posts compared to lithium disilicate and cerasmart endocrowns.In vitro study Dent J 12